Composition and performance
A two component anti rust primer composed of epoxy resin as the base material, zinc phosphate and aluminum tripolyphosphate as anti rust pigments, etc;
The paint film has good rust resistance and acid resistance;
The paint film has good oil resistance, water resistance, and wear resistance;
Fast drying and strong adhesion of paint film.
Product Usage
Suitable for seaports, ships, oil platforms, offshore facilities, bridges, mines, hydropower stations, underground pipelines, etc; The rust protection effect of various metal substrate surfaces, especially non ferrous metal surfaces such as aluminum.
Technical indicators
project
performance index 
colour
Cloud iron red, gray
Suggested film thickness
Wet film 60um/layer Dry film 40um/layer
Theoretical coating rate (㎡/kg)
5-6 days
Construction instructions
Trial period (20 ℃) 6 hours Diluent: epoxy diluent
Construction methods
Airless spraying Airless spraying Brush/roll coating
Tool cleaning
Epoxy diluent
surface treatment
The surface treatment of steel shall be carried out in accordance with the national standard "Rust Grades and Derusting Grades of Steel Surfaces before Painting" GB8923-88. The sandblasting derusting shall reach Sa2.5 level, and the manual derusting shall reach St3 level.
Construction conditions
The coating temperature range is -10-35 ℃, the relative humidity is below 85%, and the surface temperature of the substrate is above 3 ℃ above the dew point. When the substrate temperature is greater than 35 ℃, it is recommended not to apply coating. Painting cannot be carried out in adverse weather conditions such as rain, snow, wind, sand and dust.
Note: Paint should be placed in a low temperature, ventilated, and dry place; Stay away from ignition and heat sources; Store in a cool and dry place with a shelf life of one year.